CO2 sensing of La0.875Ca0.125FeO3 in wet vapor: a comparison of experimental results and first-principles calculations

Experimental results show that with an increase of relative humidity, the resistance of La0.875Ca0.125FeO3 decreases at room temperature but increases at higher temperatures (140–360 °C). The humid effect at room temperature is due to the movement of H+ or H3O+ inside of the condensed water layer on the surface of La0.875Ca0.125FeO3. Regarding the humid effect at high temperatures, the density functional theory (DFT) calculations show that H2O can be adsorbed onto the La0.875Ca0.125FeO3 surface in the molecular and dissociative adsorption configurations, where the La0.875Ca0.125FeO3 surface gains some electrons from H2O or its dissociative products, consistent with our observation. Experimental results also show that CO2 sensing response at high temperatures decreases with an increase of room-temperature relative humidity. DFT calculations indicate that CO2 adsorbed onto the La0.875Ca0.125FeO3(010) surface, where high concentration oxygen adsorption occurs without water adsorption nearby, releases some electrons into the semiconductor surface, playing the role of a donor. The interaction between CO2 and the local La0.875Ca0.125FeO3(010) surface with pre-adsorption of H2O nearby results in some electron transfer from the La0.875Ca0.125FeO3 surface to CO2, which is responsible for the weakening of CO2 response at high temperatures for La0.875Ca0.125FeO3 with an increase of room-temperature relative humidity.